Effect of post annealing on microstructure and mechanical properties in Ni-free N-containing ODS steel
A. Kowalska-Mori , H. Mamiya , M. Ohnuma , J. Ilavsky , E.P. Gilbert , Piotr Bazarnik , H. Kitazawa , Małgorzata Lewandowska
AbstractThe precipitation behavior of Y2O3 and MnO nanoparticles after isothermal treatment, in a Ni-free N-containing oxide dispersion strengthened (ODS) steel was studied by wide-angle X-ray scattering (WAXS), ultra-small-angle and small-angle X-ray scattering (USAXS/SAXS), small angle neutron scattering (SANS) and scanning transmission electron microscopy (STEM). Mechanical properties were investigated via tensile and micro-hardness testing. Additional precipitation occurred during annealing, in addition to the precipitates formed during sintering. The highest volume distribution of Y2O3, with average size of 6 nm, was determined by alloy contrast variation (ACV) analysis of SAXS and SANS for the sample annealed at 800 °C; this sample shows the highest hardness and ultimate tensile strength. Above that temperature, coarsening of both matrix and precipitates and depletion of nitrogen from matrix degraded the mechanical properties. The very fine nanoparticles and thermally induced dissolution of nitrogen influenced mechanical properties.
|Journal series||Materials Characterization, ISSN 1044-5803, (A 40 pkt)|
|Publication size in sheets||0.5|
|Keywords in English||ODS austenitic steel Nanoparticle Small-angle neutron scattering (SANS), Ultrasmall- angle X-ray scattering (USAXS) Alloy contrast variation (ACV)|
|ASJC Classification||; ; ;|
|Score||= 40.0, 28-05-2019, ArticleFromJournal|
|Publication indicators||: 2017 = 1.545; : 2017 = 2.892 (2) - 2017=3.036 (5)|
* presented citation count is obtained through Internet information analysis and it is close to the number calculated by the Publish or Perish system.