Structure and mechanical properties of TiB 2 /TiC – Ni composites fabricated by pulse plasma sintering method
Konrad Cymerman , Dariusz Oleszak , Marcin Rosiński , Andrzej Michalski
AbstractTiB2/TiC – Ni composites were synthesized starting from the powders of Ti, B4C and Ni, using Pulse Plasma Sintering (PPS) method. Typically used one - step (1100°C–10 min.) and novel double-step sintering processes (900°C–10 min. +1100°C–5 min.) were applied and compared. XRD studies showed that the composite obtained by double-step sintering consisted of TiB2, TiC and Ni phases. For one-step pro-cessing additionally undesired Ni3B and graphite were detected. SEM observations revealed dark-grey grains of TiB2, light-grey grains of TiC (both around 25 mm in size) and Ni areas surrounded by TiC. The composites synthesized in one - and double - step processes revealed the hardness and relative density of 2335 HV5 (±110) and 97.8% and 2470 HV5 (±70) and 99.8%, respectively. Novel double - step sintering process allowed to avoid undesired phases (graphite, Ni3B) and only TiB2, TiC and Ni were present in the structure. Additionally it was possible to decrease the temperature of the process comparing to other fabrication methods.
|Journal series||Advanced Powder Technology, ISSN 0921-8831, (A 30 pkt)|
|Publication size in sheets||0.5|
|Keywords in Polish||kompozyty TiB2/TiC – Ni, spiekanie, impulsowe spiekanie plazmowe|
|Keywords in English||TiB2/TiC – Ni composites, sintering, pulse plasma sintering|
|Score||= 30.0, 18-12-2019, ArticleFromJournal|
|Publication indicators||= 4; = 3; : 2018 = 1.271; : 2018 = 3.25 (2) - 2018=3.101 (5)|
* presented citation count is obtained through Internet information analysis and it is close to the number calculated by the Publish or Perish system.